AN APFIM STUDY OF THE AGEING BEHAVIOUR OF U-6.0 wt% NbReportar como inadecuado




AN APFIM STUDY OF THE AGEING BEHAVIOUR OF U-6.0 wt% Nb - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.



Abstract : Atom Probe Field Ion Microscopy APFIM in conjunction with Transmission Electron Microscopy is being used to determine the mechanisms responsible for the strength increase observed upon ageing U-6.0wt% Nb. Analysis of composition profiles obtained from the APFIM show that two distinct types of phase separation reactions are taking place during ageing. At present no conclusive evidence exists to identify the reaction mechanisms. However, electron diffraction and APFIM results suggest that at ageing temperatures below 400°C a fine sale segregation reaction takes place, possibly spinodal decomposition, whilst at temperatures above 400°C strengthening is probably due to precipitation of a Nb-rich phase.





Autor: G. Beverini D. Edmonds

Fuente: https://hal.archives-ouvertes.fr/



DESCARGAR PDF




Documentos relacionados