Poly Aryl Ether Ketones PAEKs and carbon-reinforced PAEK powders for laser sinteringReportar como inadecuado

Poly Aryl Ether Ketones PAEKs and carbon-reinforced PAEK powders for laser sintering - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.

Journal of Materials Science

, Volume 52, Issue 10, pp 6004–6019

First Online: 06 February 2017Received: 19 October 2016Accepted: 24 January 2017DOI: 10.1007-s10853-017-0840-0

Cite this article as: Chen, B., Wang, Y., Berretta, S. et al. J Mater Sci 2017 52: 6004. doi:10.1007-s10853-017-0840-0


This paper discusses various methods of fabrication of plain and carbon-reinforced composite powders, as well as a range of powder characterisation test methods suitable for defining powders for laser sintering. Two milling processes based on disc blades and rotatory cutting knives were used as methods of fabrication of powders, starting from injection moulding granule grades, for comparison with current powders obtained directly from polymerisation processes. It was found that the milling process affects the particles properties. The rotary milling produced powders with superior properties in comparison with the disc milling method. Tests including particle size distribution, angle of repose, aspect ratio, sphericity and roundness of particles were employed to compare and assess the suitability of powders for laser sintering. The Brunauer–Emmett–Teller test was identified as a useful method to define surface roughness and porosity of the particles. The carbon fibre Cf Poly Ether Ketone PEK granules milled well and after an additional sieving process created a good quality powder. This is the first attempt to investigate properties of PEK powder with encapsulated Cf and follow their sintering profile through hot-stage microscopy. It is expected that this type of composite powder will create isotropic structures in comparison with the highly anisotropic properties given by the known dry mix composite powders, currently used in laser sintering.

Autor: Binling Chen - Yuan Wang - Silvia Berretta - Oana Ghita

Fuente: https://link.springer.com/