Effective Red Compensation of  :  Phosphor by Codoping Ions and Its Energy TransferReportar como inadecuado

Effective Red Compensation of  :  Phosphor by Codoping Ions and Its Energy Transfer - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.

Journal of NanomaterialsVolume 2012 2012, Article ID 848274, 7 pages

Research ArticleCollege of Materials Science and Engineering, Nanjing University of Technology, Jiangsu, Nanjing 210009, China

Received 15 August 2012; Accepted 28 September 2012

Academic Editor: Su Chen

Copyright © 2012 Le Zhang et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.



ions codoped Sr2SiO4 : Dy

phosphors were prepared by the solid-state reaction method using NH4Cl as the flux. Their phase compositions, photoluminescence properties, and the energy transfer process were systematically investigated. All Mn-Dy codoped powders were ′-Sr2SiO4. The codoping concentration range of Mn

was  mol% to keep the structure undamaged. The broad red emission of Mn

centered at 647 nm in Sr2SiO4 : Mn, Dy powders, which effectively compensated the red emission of Sr2SiO4 : Dy

phosphor. The CIE chromaticity coordinates dramatically changed from 0.310, 0.340 to 0.332, 0.326 due to the red enhancement via the energy transfer from Dy

to Mn

. This energy transfer is realized by the exchange interaction. But the luminescence quenching of Sr2SiO4 : Dy, Mn phosphor was mainly caused by the electric multipoles interaction. The concentration optimized Sr0.96, Mn0.02, Dy0.022SiO4 phosphor with high and almost pure white emission has great potential to act as a single-matrix white phosphor for white LEDs.