Nucleation and Growth of the Ni5Al3 Phase in Ni-Al Austenite and MartensiteReportar como inadecuado




Nucleation and Growth of the Ni5Al3 Phase in Ni-Al Austenite and Martensite - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.



Abstract : The nucleation and growth mechanisms of Ni5Al3 precipitates and microtwinned plates in B2 austenite and 2M 3R martensite phases are described on the basis of conventional and high resolution electron microscopy. In the Ni62.5Al37.5 B2 austenite matrix short annealings at 550°C introduce three-pointed star shaped precipitates consisting of twin related parts of different variants of the Ni5Al3 structure. Longer annealings result in plates growing separately from these wings and developing microtwinning in order to accommodate stress built-up at the interfaces with the surrounding matrix. Annealing of Ni65Al35 2M martensite plates induces simple reordering into the Ni5Al3 phase, increasing the fct c-a ratio by about 1%. As a result stracking faults are introduced in the smallest twin variants.





Autor: D. Schryvers L. Toth Y. Ma L. Tanner

Fuente: https://hal.archives-ouvertes.fr/



DESCARGAR PDF




Documentos relacionados