Abstract : Thin film deposition by laser irradiation of FeCO5 at two radiation wavelengths 248 nm and 488 nm was performed. A perpendicular geometry of irradiation was used. Maximum deposition rates of 14 Å-s at λ = 248 nm and 1.5 Å-s at λ = 488 nm were obtained, indicating a diffusion limited process. SEM analysis of film morphologies showed significant differencies in the nucleation and growth of films deposited at 248 nm and 488 nm. XPS surface analysis revealed a higher carbon content and carbidic phases in the surface of films deposited at 488 nm on SiO2 quartz substrates. Oxidized surface Fe phases were found in films, with increasing the exposure time to laser radiation. The film properties are discussed in connection with irradiation conditions and specific mechanisms involved.





Autor: I. Voicu R. Alexandrescu R. Cireasa I. Morjan D. Dumitras S. Mulenko A. Pogorelyi A. Andrei

Fuente: https://hal.archives-ouvertes.fr/



DESCARGAR PDF




Documentos relacionados