Micro and Nano Structure of Electrochemically Etched Silicon Epitaxial WafersReportar como inadecuado




Micro and Nano Structure of Electrochemically Etched Silicon Epitaxial Wafers - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.

Croatica Chemica Acta, Vol.85 No.1 April 2012. -

Silicon epitaxial wafers, consisting of 280 μm thick n-type substrate layer and 4–5 μm thick epitaxial layer, were electrochemically etched in hydrofluoric acid ethanol solution, to produce porous silicon samples. The resistivity of epitaxial layer was 1 Ω cm, while the substrate was much better conductor with resistivity 0.015 Ω cm. By varying the etching time, the micro- and nano-pores of different sizes were obtained within the epitaxial layer, and on the substrate surface. Due to the lateral etching the epitaxial layer was partially detached from the substrate and could be peeled off. The influence of etching time duration on the optical and structural properties of porous samples was investigated by Raman, infrared and photoluminescence spectroscopy. The samples were analysed immediately after the etching and six months later, while being stored in ambient air. The Raman spectra showed the shift in positions of transversal optical TO phonon bands, between freshly etched samples and the one stored in ambient air. Infrared spectra indicated the presence of SiHx species in the freshly etched samples, and appearance of oxidation after prolonged storage. Photoluminescence spectra were very weak in freshly etched samples, but their intensity has increased substantially in six month period. doi: 10.5562-cca1971

nano materials; silicon; electrochemistry; raman; infrared



Autor: Ozren Gamulin - ; University of Zagreb, School of Medicine, Department of Physics and Biophysics, Šalata 3b, 10 000, Zagreb, Cro

Fuente: http://hrcak.srce.hr/



DESCARGAR PDF




Documentos relacionados