Microstructure of Rehandled Layer on the Surface of Nano-CuCr AlloyReportar como inadecuado




Microstructure of Rehandled Layer on the Surface of Nano-CuCr Alloy - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.

Nano-CuCr25 and nano-CuCr50 alloys are prepared by vacuum hot pressing using powders activated by high energy ball-milling. The surface of the alloys after arc erosion and the rehandled layer are studied. The depth of the rehandled layer on nano-CuCr50 is found to be 3~6 micrometers at low current and the microstructure is refined. At high-current,the rehandled layer of nano-CuCr25 is found to be about 3~4 micrometers. Compared with normal CuCr25 alloy, nano-CuCr25 is more stable as cathode. Anode spots which can destroy the contact occur at high-current. Arc energy of nano-CuCr25 is lower than that of normal CuCr25 alloy.

KEYWORDS

nano-CuCr alloys; rehandled layer; microstructure; vacuum arc energy

Cite this paper







Autor: Jia Cheng, Heng Zhang, Zhi-mao Yang, Bing-jun Ding

Fuente: http://www.scirp.org/



DESCARGAR PDF




Documentos relacionados