Sorption of CuII Ions on Chitosan-Zeolite X Composites: Impact of Gelling and Drying ConditionsReportar como inadecuado

Sorption of CuII Ions on Chitosan-Zeolite X Composites: Impact of Gelling and Drying Conditions - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.


Institut Charles Gerhardt, UMR 5253 CNRS-UM2-ENSCM-UM1, Matériaux Avancés pour la Catalyse et la Santé, ENSCM, 8 rue Ecole Normale, 34296 Montpellier Cedex 5, France


Laboratoire de Chimie Des Matériaux, Département de Chimie, Faculté des Sciences Exactes et Appliquées, Université Oran 1-Ahmed Benbella, B.P. 1524 Elmenaouar, Oran 31000, Algeria


Faculté de Chimie, Université des Sciences et de la Technologie d’Oran-Mohamed Boudiaf, USTO, B.P. 1505 Elmenaouar, Oran 31000, Algeria


Author to whom correspondence should be addressed.

Academic Editor: Massimiliano Fenice

Abstract Chitosan-zeolite Na-X composite beads with open porosity and different zeolite contents were prepared by an encapsulation method. Preparation conditions had to be optimised in order to stabilize the zeolite network during the polysaccharide gelling process. Composites and pure reference components were characterized using X-ray diffraction XRD; scanning electron microscopy SEM; N2 adsorption–desorption; and thermogravimetric analysis TG. CuII sorption was investigated at pH 6. The choice of drying method used for the storage of the adsorbent severely affects the textural properties of the composite and the copper sorption effectiveness. The copper sorption capacity of chitosan hydrogel is about 190 mg·g−1. More than 70% of this capacity is retained when the polysaccharide is stored as an aerogel after supercrititcal CO2 drying, but nearly 90% of the capacity is lost after evaporative drying to a xerogel. Textural data and CuII sorption data indicate that the properties of the zeolite-polysaccharide composites are not just the sum of the properties of the individual components. Whereas a chitosan coating impairs the accessibility of the microporosity of the zeolite; the presence of the zeolite improves the stability of the dispersion of chitosan upon supercritical drying and increases the affinity of the composites for CuII cations. Chitosan-zeolite aerogels present CuII sorption properties. View Full-Text

Keywords: biomass; chitosan; zeolite X; composites; aerogel; metal sorption biomass; chitosan; zeolite X; composites; aerogel; metal sorption

Autor: Amal Djelad 1,2, Amine Morsli 3, Mike Robitzer 1, Abdelkader Bengueddach 2, Francesco di Renzo 1 and Françoise Quignard 1,*