Composition Distribution and Electrochemical Behavior of an Ni2Al3 Coating on Q235 SteelReportar como inadecuado




Composition Distribution and Electrochemical Behavior of an Ni2Al3 Coating on Q235 Steel - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.

Engineering Research Center of Materials Behavior and Design, Ministry of Education, Nanjing University of Science and Technology, Nanjing 210094, China





*

Author to whom correspondence should be addressed.



Academic Editor: Hugo F. Lopez

Abstract An Ni2Al3 coating was prepared via the electrodeposition of nickel followed by pack aluminization. Polarization curve and electrochemical impedance spectroscopy were performed to study the room temperature corrosion behavior of the coating in a 3.5 wt. % NaCl solution. The long-term impedance of the coating was also investigated after immersion for 30 days. Results show that the Ni2Al3 coating possessed lower corrosion current density Icorr and higher polarization resistance Rp than the substrate in the solution. The Bode plots of the coating showed two time constants after the long-term immersion. Pitting corrosion was found on the coating surface. View Full-Text

Keywords: Ni2Al3 coating; polarization curve; electrochemical impedance spectroscopy; pitting corrosion Ni2Al3 coating; polarization curve; electrochemical impedance spectroscopy; pitting corrosion





Autor: Ningning Li, Minzhi Wang, Gong Zheng, Yongsheng Li and Guang Chen *

Fuente: http://mdpi.com/