Electrochemical Surface Treatment of a β-titanium Alloy to Realize an Antibacterial Property and BioactivityReportar como inadecuado




Electrochemical Surface Treatment of a β-titanium Alloy to Realize an Antibacterial Property and Bioactivity - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.

1

Institute of Biomaterials and Bioengineering, Tokyo Medical and Dental University, Chiyoda, Tokyo 101-0062, Japan

2

Graduate School of Engineering, The University of Tokyo, Bunyko, Tokyo 113-8656, Japan

3

Institute for Materials Research, Tohoku University, Sendai, Miyagi 980-8577, Japan

4

Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University, Bunkyo, Tokyo 113-0034, Japan





*

Author to whom correspondence should be addressed.



Academic Editors: Vineet V. Joshi and Alan Meier

Abstract In this study, micro-arc oxidation MAO was performed on a β-type titanium alloy, namely, Ti-29Nb-13Ta-4.6Zr alloy TNTZ, to improve not only its antibacterial property but also bioactivity in body fluids. The surface oxide layer formed on TNTZ by MAO treatment in a mixture of calcium glycerophosphate, calcium acetate, and silver nitrate was characterized using surface analyses. The resulting porous oxide layer was mainly composed of titanium oxide, and it also contained calcium, phosphorus, and a small amount of silver, all of which were incorporated from the electrolyte during the treatment. The MAO-treated TNTZ showed a strong inhibition effect on anaerobic Gram-negative bacteria when the electrolyte contained more than 0.5 mM silver ions. The formation of calcium phosphate on the surface of the specimens after immersion in Hanks’ solution was evaluated to determine the bioactivity of TNTZ with sufficient antibacterial property. As a result, thick calcium phosphate layers formed on the TNTZ specimen that underwent MAO treatment, whereas no precipitate was observed on TNTZ without treatment. Thus, the MAO treatment of titanium-based alloys is confirmed to be effective in realizing both antibacterial and bioactive properties. View Full-Text

Keywords: titanium alloy; micro-arc oxidation; antibacterial property; bioactivity; hard-tissue compatibility titanium alloy; micro-arc oxidation; antibacterial property; bioactivity; hard-tissue compatibility





Autor: Yusuke Tsutsumi 1,2,* , Mitsuo Niinomi 3, Masaaki Nakai 3, Masaya Shimabukuro 4, Maki Ashida 1, Peng Chen 1, Hisashi Doi 1 and Takao Hanawa 1