Preparation and Elastic Moduli of Germanate Glass Containing Lead and BismuthReportar como inadecuado

Preparation and Elastic Moduli of Germanate Glass Containing Lead and Bismuth - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.

Department of Physics, Faculty of Science, Universiti Putra Malaysia, 43400 UPM Serdang, Selangor, Malaysia


Author to whom correspondence should be addressed.

Abstract This paper reports the rapid melt quenching technique preparation for the new family of bismuth-lead germanate glass BPG systems in the form of GeO260–PbO40−x–½Bi2O3x where x = 0 to 40 mol%. Their densities with respect of Bi2O3 concentration were determined using Archimedes’ method with acetone as a floatation medium. The current experimental data are compared with those of bismuth lead borate B2O320–PbO80−x–Bi2O3x. The elastic properties of BPG were studied using the ultrasonic pulse-echo technique where both longitudinal and transverse sound wave velocities have been measured in each glass samples at a frequency of 15 MHz and at room temperature. Experimental data shows that all the physical parameters of BPG including density and molar volume, both longitudinal and transverse velocities increase linearly with increasing of Bi2O3 content in the germanate glass network. Their elastic moduli such as longitudinal, shear and Young’s also increase linearly with addition of Bi2O3 but the bulk modulus did not. The Poisson’s ratio and fractal dimensionality are also found to vary linearly with the Bi2O3 concentration. View Full-Text

Keywords: glasses; bismuth; lead; germanate; elastic moduli glasses; bismuth; lead; germanate; elastic moduli

Autor: Hj A. A. Sidek * , Hamid R. Bahari, Mohamed K. Halimah and Wan M. M. Yunus