Oxide ceramics of La1.85Sr0.15CuO4-d LSCuO were grown by using the solid-state reaction method. The oxygen stoichiometry was modified by submitting the obtained samples to a post-growth thermal process at 9000C under an inert atmosphere. Powder X-ray diffraction analysis shows all samples are single-phase with K2NiF4-type structure. The thermoelectric properties were studied from Seebeck coeficient ST and electrical resistivity ρT measurements in the temperature range from 90 to 290K. The magnitude of ST and ρ T increases with the processing time reaching maximum values, at room temperature, close 150μV-K and 0:8m Ω - cm, respectively. From ST and ρ T data it was possible to calculate the thermoelectric power factor PF, which reaches maximum values close to 38μW-K2cm in the temperature range between 90 and 160K. The behavior of the transport properties and PF becomes these ceramics promissory thermoelectric materials, which could be used in low temperature thermoelectric applications., Utilizando el método de reacción sólida fue posible preparar muestras policristalinas de La1.85Sr0.15CuO4-d LSCuO. La estequiometría del oxígeno fue alterada sometiendo las muestras a un proceso térmico a 900oC en una atmósfera inerte. La difracción de rayos-X mostró la presencia de compuestos monofásicos con una estructura del tipo K2NiF4. Las propiedades termoeléctricas fueron estudiadas a partir de mediciones de coeficiente Seebeck ST y resistividad eléctrica ρT en el rango de temperatura entre 90 y 290K. La magnitud de ST y ρT se incrementa con el tiempo de desoxigenación alcanzando valores máximos cercanos a 150μV-K y 0:8m Ω cm, respectivamente. A partir de las mediciones de ST y ρT se determinó el factor de potencia termoeléctrico, el cual alcanza valores máximos cercanos a 38μW-K2 - cm, en el rango de temperatura entre 90 y 160K. El comportamiento de las propiedades de transporte y los valores alcanzados por el factor de potencia convierten estas cerámicas en materiales promisorios para ser utilizados en aplicaciones termoeléctricas.

Tipo de documento: Artículo - Article

Palabras clave: Thermoelectric materials, Transport properties, LSCuO compounds, Figure of merit., Materiales termoeléctricos, Propiedades de transporte, Compuestos de LSCuO, Figura de mérito.





Source: http://www.bdigital.unal.edu.co


Teaser



momento Revista de Fı́sica, No 39, Diciembre 2009 67 LSCuO ceramics as possible material for thermoelectric energy conversion J.
E.
Rodrı́guez1 1 Departamento de Fı́sica Unversidad Nacional de Colombia Grupo de Materiales Termoeléctricos Abstract Oxide ceramics of La1.85 Sr0.15 CuO4−δ (LSCuO) were grown by using the solid-state reaction method.
The oxygen stoichiometry was modified by submitting the obtained samples to a post-growth thermal process at 9000 C under an inert atmosphere.
Powder X-ray diffraction analysis shows all samples are single-phase with K2 N iF4 -type structure. The thermoelectric properties were studied from Seebeck coefficient S(T ) and electrical resistivity ρ(T ) measurements in the temperature range from 90 to 290K.
The magnitude of S(T ) and ρ(T ) increases with the processing time reaching maximum values, at room temperature, close 150µV -K and 0.8mΩ − cm, respectively.
From S(T) and ρ(T ) data it was possible to calculate the thermoelectric power factor PF, which reaches maximum values close to 38µW-K 2 cm in the temperature range between 90 and 160K.
The behavior of the transport properties and PF becomes these ceramics promissory thermoelectric materials, which could be used in low temperature thermoelectric applications. Keywords: Thermoelectric materials, Transport properties, LSCuO compounds, Figure of merit. Resumen Utilizando el método de reacción sólida fué posible preparar muestras policristalinas de La1.85 Sr0.15 CuO4−δ (LSCuO). La estequiometrı́a del oxı́geno fué alterada sometiendo las J.E.
Rodrı́guez: e-mail: jerodriguezl@unal.edu.co 68 J.E.
Rodrı́guez muestras a un proceso térmico a 9000 C en una atmósfera inerte.
La difracción de rayos-X mostró la presencia de compuestos monofasicos con una estructura del tipo K2 N iF4 . Las propiedades termoeléctricas fueron estudiadas a partir de mediciones de coeficiente Seebeck S(T ) y resistividad eléctrica ρ(T ) en el ran...