Nanocrystal and surface alloy properties of bimetallic Gold-Platinum nanoparticlesReportar como inadecuado




Nanocrystal and surface alloy properties of bimetallic Gold-Platinum nanoparticles - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.

Nanoscale Research Letters

, 2:12

First Online: 30 November 2006Received: 06 August 2006Accepted: 16 September 2006

Abstract

We report on the correlation between the nanocrystal and surface alloy properties with the bimetallic composition of gold-platinumAuPt nanoparticles. The fundamental understanding of whether the AuPt nanocrystal core is alloyed or phase-segregated and how the surface binding properties are correlated with the nanoscale bimetallic properties is important not only for the exploitation of catalytic activity of the nanoscale bimetallic catalysts, but also to the general exploration of the surface or interfacial reactivities of bimetallic or multimetallic nanoparticles. The AuPt nanoparticles are shown to exhibit not only single-phase alloy character in the nanocrystal, but also bimetallic alloy property on the surface. The nanocrystal and surface alloy properties are directly correlated with the bimetallic composition. The FTIR probing of CO adsorption on the bimetallic nanoparticles supported on silica reveals that the surface binding sites are dependent on the bimetallic composition. The analysis of this dependence further led to the conclusion that the relative Au-atop and Pt-atop sites for the linear CO adsorption on the nanoparticle surface are not only correlated with the bimetallic composition, but also with the electronic effect as a result of the d-band shift of Pt in the bimetallic nanocrystals, which is the first demonstration of the nanoscale core-surface property correlation for the bimetallic nanoparticles over a wide range of bimetallic composition.

KeywordsGold-Platinum nanoparticles Nanocrystal alloy Surface binding sites Bimetallic composition Electronic supplementary materialThe online version of this article doi:10.1007-s11671-006-9022-8 contains supplementary material, which is available to authorized users.

Download fulltext PDF



Autor: Derrick Mott - Jin Luo - Andrew Smith - Peter N. Njoki - Lingyan Wang - Chuan-Jian Zhong