On Improving the Formability of AA6061-SiCp Composite Synthesized Using Friction Stir ProcessingReportar como inadecuado




On Improving the Formability of AA6061-SiCp Composite Synthesized Using Friction Stir Processing - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.

1 Anna University, Chennai

Abstract : Friction stir processing FSP is a potentially useful method for producing composites of enhanced surface properties. In this work, an AA6061-SiCp composite, synthesized using FSP, was tested in three-point bending and uni-axial hot tensile and bi-axial stressing to assess its formability. Bending test results reveal an increased bending strength in the composite compared with the AA 6061 alloy, subjected to FSP, but without the addition of the SiC particles. Based on the hot tensile tests, the biaxial stressing temperatures were fixed as 623 K and 673 K. Bi-axial stressing reveals that a maximum bulge height of 18 mm could be obtained by forming into a cavity of 59 mm diameter at a pressure of 0.2 MPa. Based on the results, process parameters such as formed bulge height, forming time, strain rate and strain rate sensitivity index were determined. In the present experiments, the strain rate sensitivity index increased with increasing forming pressure and reached a maximum value of 0.40 at a forming pressure of 0.25, as the latter variable was increased from 0.20 to 0.25 MPa. Microstructures and forming limit diagram of the composite were obtained and analysed in detail. The present findings can pave the way for the commercial exploitation of FSP-technology-based, efficient processing of the AA6061-SiCp composite.

Keywords : Friction stir processing Formability Three-point bending test Forming limit diagram





Autor: M Puviyarasan - V S Senthil Kumar - D Viswanathan - K A Padmanabhan -

Fuente: https://hal.archives-ouvertes.fr/



DESCARGAR PDF




Documentos relacionados