Microwave-Assisted Synthesis of Mixed Metal-Oxide NanoparticlesReportar como inadecuado




Microwave-Assisted Synthesis of Mixed Metal-Oxide Nanoparticles - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.

Journal of NanoparticlesVolume 2013 2013, Article ID 737831, 11 pages

Research Article

School of Chemical Sciences, Devi Ahilya University, Indore 452001, India

Laser Materials Development and Devices Division, RRCAT, Indore 452013, India

Received 21 January 2013; Accepted 9 February 2013

Academic Editor: Amir Kajbafvala

Copyright © 2013 Akrati Verma et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Nanoparticles of mixed metal oxides, ZrO2, ZrTiO4, and ZrV2O7 were prepared by microwave-assisted citrate sol-gel and solution combustion method. The prepared nanoparticles were characterized for their structural details using XRD and TEM techniques. The broadening of Raman bands is ascribed to local compositional fluctuations or local positional disordering produced due to random distribution of Zr

and Ti

between equivalent sites. The XPS spectra confirm the incorporation of Ti in ZrO2 and suggest Zr as well as Ti in +4 oxidation state. Gelation and fast combustion seem to be the reason for smaller particle sizes. ZrV2O7 nanocrystalline material was synthesized by microwave- assisted solution combustion method. Low angle powder XRD measurements confirm the mesoporous nature of the prepared material. The effect of calcination temperature on the phase transformation of the materials has been investigated. Among tetragonal, monoclinic, and cubic phases, the monoclinic phase is predominant at higher calcinations temperature. The XPS confirms the incorporation of V2O5 in ZrO2 and suggests that Zr and V are in the same oxidation state +4. The average particle sizes for ZrO2, ZrTiO4, and ZrV2O7 were found to be in the ranges of 5–10 nm, 2–5 nm, and 10–50 nm, respectively.





Autor: Akrati Verma, Reena Dwivedi, R. Prasad, and K. S. Bartwal