Environmental Impacts on the Strength Parameters of Mineral-Acrylic PMMA-ATH Facade Panels - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.

International Journal of Polymer ScienceVolume 2015 2015, Article ID 134714, 5 pages

Research ArticleBuilding and Structure Physics Division, Institute of Building Materials and Structures, Faculty of Civil Engineering, Cracow University of Technology, 31-155 Cracow, Poland

Received 6 August 2015; Revised 15 November 2015; Accepted 17 November 2015

Academic Editor: Gonzalo Martínez-Barrera

Copyright © 2015 Aleksander Byrdy and Michał Kołaczkowski. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Composite mineral-acrylic panels consist in 80% of natural minerals produced from bauxite aluminium hydroxides ATH and in 20% from acrylic resin polymethyl methacrylate PMMA. This material due to high usability is widely used in interior finishes. Recently, the mineral-acrylic panels have been used as external claddings of buildings. So far, there are several dozen elevations realized worldwide. Due to the variability of the strength parameters of PMMA acrylic resins depending on the environmental influence, a number of tests on samples of mineral-acrylic panels to verify their suitability for use in climate conditions in Central Europe were performed. The studies determined the change of the material parameters after being subjected to aging process in conditions of high temperature, high relative humidity, freeze-thaw cycles, and UV radiation. In the studies parameters such as flexural strength and modulus of elasticity were measured at a reference temperature of 23°C. In raised and lowered temperatures only the tensile strength tests were conducted. Due to the lack of information in the available literature, the authors carried out tests of the temperature influence on the PMMA-ATH composite modulus of elasticity and flexural strength which is crucial in designing process.





Autor: Aleksander Byrdy and Michał Kołaczkowski