In Situ Degradation of Chitosan-Polygalacturonic Acid-Hydroxyapatite Nanocomposites in Cell Culture MediaReportar como inadecuado




In Situ Degradation of Chitosan-Polygalacturonic Acid-Hydroxyapatite Nanocomposites in Cell Culture Media - Descarga este documento en PDF. Documentación en PDF para descargar gratis. Disponible también para leer online.

International Journal of Polymer ScienceVolume 2010 2010, Article ID 175264, 12 pages

Research ArticleDepartment of Civil Engineering, North Dakota State University, Fargo, ND 58105, USA

Received 12 February 2010; Revised 22 March 2010; Accepted 22 March 2010

Academic Editor: Shanfeng Wang

Copyright © 2010 Rohit Khanna et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

The molecular and mechanical characteristics of in situ degradation behavior of chitosan-polygalacturonic acid-hydroxyapatite Chi-PgA-HAP nanocomposite films is investigated using Fourier Transform Infrared spectroscopy FTIR, Atomic Force Microscopy AFM, and modulus mapping techniques for up to 48 days of soaking in cell culture media. The surface molecular structure of media-soaked samples changes over the course of 48 days of soaking, as indicated by significant changes in phosphate vibrations 1200–900  indicating apatite formation. Chitosan-Polygalacturonic acid polyelectrolyte complexes PECs govern structural integrity of Chi-PgA-HAP nanocomposites and FTIR spectra indicate that PECs remain intact until 48 days of soaking. In situ AFM experiments on media-soaked samples indicate that soaking results in a change in topography and swelling proceeds differently at the initial soaking periods of about 8 days than for longer soaking. In situ modulus mapping experiments are done on soaked samples by probing 1–3 nm of surface indicating elastic moduli of 4 GPa resulting from proteins adsorbed on Chi-PgA-HAP nanocomposites. The elastic modulus decreases by 2 GPa over a long exposure to cell culture media 48 days. Thus, as water enters the Chi-PgA-HAP sample, surface molecular interactions in Chi-PgA-HAP structure occur that result in swelling, causing small changes in nanoscale mechanical properties.





Autor: Rohit Khanna, Kalpana S. Katti, and Dinesh R. Katti